椰殼活性炭是一種多孔徑的炭化物，有著極其豐富的孔隙構造，具有很好的吸附性能。它的吸附作用集物理及化學的吸咐力而成的，其外觀色澤呈黑色，其成份除了主要的炭以外，還包含了少量的氫、氮、氧，其結構則外形似以一個六邊形，由于不規則的六邊形結構，確定了其多也體枳及高表面積的特點，每克的活性炭所具的有比表面相當于1000個平方米之多。

Coconut shell activated carbon is a kind of multiple aperture of carbon, has the extremely rich pore structure, has the very good adsorption performance. Its adsorption set of physical and chemical adsorption force, and its appearance in black color, its ingredients, except the main carbon also contains a small amount of hydrogen, nitrogen, oxygen, and its structure looks like in a hexagon, due to the irregular hexagon structure, identified the more definite and also the characteristics of high surface area, per gram of activated carbon to the surface of the than equivalent to more than 1000 square meters.

椰殼活性炭炭化過程：

步，炭化，將原料在170至600的溫度下干燥，同量將其80有機組織炭化。

步，活化，將 步已炭化好的炭化料送入反應爐中，與活化劑和水蒸氣反應，完成其活化過程，制成成品。在吸熱反應過程中，主要產生CO及H2組合氣體，用以將炭化料加熱至適當的溫度(800至1000度)，除去其所有可分解物，產生豐富的孔隙結構及巨大的比表面積，使椰殼活性炭具有很強的吸附力。不同的原料生產的椰殼活性炭具有不同的孔徑，其中以椰殼為原料的椰殼活性炭的孔徑 小，木質椰殼活性炭的也孔徑一般較大，煤質椰殼活性炭的孔徑介于兩者間。椰殼活性炭孔徑一般分為三類：大孔：1A過渡孔：20-1000A微孔：20A根據以上特性可以看出，針對不同的吸附對象，需選用相應的椰殼活性炭，以做到 的性價比。因此，一般在液相吸附中，應選用較多過渡孔徑及平均孔徑較大的椰殼活性炭。

Coconut shell activated carbon carbonization process:

The first step, coking, the raw material from 170 to 170 under the temperature of drying, the same amount of its 80 organic tissue charring.

The second step, activation, will be the first step is carbonized good carbonized material into reactor, and activator and water vapor reaction, to complete the activation process, made into finished products. Main produces in the process of endothermic reaction, CO and H2 gas used to heat the carbonized material to proper temperature (800-1000 degrees), remove all its decomposable material, produce abundant pore structure and huge specific surface area, make the coconut shell activated carbon has very strong adsorption capacity. Different raw material to produce coconut shell activated carbon with different aperture, among them with coconut shell as raw materials of the coconut shell activated carbon minimum aperture, woodiness coconut shell activated carbon Aperture also generally larger, coal quality coconut shell activated carbon aperture somewhere in between. Coconut shell activated carbon pore size generally fall into three categories: big hole: 1 A transition hole: 20-1000 - A microporous: 20 A, according to the above features can be seen, according to different object, adsorption to choose corresponding coconut shell activated carbon, to be the best price. Therefore, generally in the liquid phase adsorption, should choose more transition pore diameter and average pore diameter larger coconut shell activated carbon.